Machining Data for Face Machining

MIFR/ MIFR 10 MIFR 15
GFQR PICCO MEFL IC908 IC908
Tensile Cutting IC528 IC228 8 IC908 Feed Feed
Strength Hardness Material Speed Feed Feed Feed
Material Condition [N/mm2] (mm/rev) (mm/rev) (mm/rev) (mm/rev) (mm/rev)
HB No. (m/min)

< 0.25 %C Annealed 420 125 1 80-180 0.02-0.08 0.015-0.05
190 2
>= 0.25 %C Annealed 650

Non-alloy Quenched

steel and < 0.55 %C and 850 250 3 80-130 0.02-0.06 0.015-0.04
220 4
cast steel, tempered

free cutting >= 0.55 %C Annealed 750
steel Quenched

and 1000 300 5 80-120 0.02-0.06 0.015-0.04
0.015-0.08 0.03-0.10 0.03-0.08
tempered
200 6 80-140 0.02-0.08 0.015-0.04
P Low alloy and cast Annealed 600 275 7 80-140 0.02-0.08 0.015-0.04
steel (less than 5% of 930 300 8 80-120 0.02-0.06 0.015-0.03
alloying elements) Quenched 1000 350 9 80-120 0.02-0.05 0.015-0.03
and 1200 200 10 80-140 0.02-0.08 0.015-0.04

tempered

Annealed 680

High alloyed steel, cast Quenched 1100 325 11 80-120 0.02-0.08 0.015-0.03
steel, and tool steel and

tempered

Stainless steel Ferritic/ 680 200 12 40-120 0.02-0.08 0.015-0.04 0.015-0.07 0.03-0.08 0.02-0.05
and cast steel martensitic 820 240 13 40-120 0.02-0.07 0.015-0.04 0.015-0.07 0.03-0.08 0.02-0.05
180 14 40-100 0.02-0.06 0.015-0.03 0.015-0.07 0.03-0.08 0.02-0.05
Martensitic
180
M Stainless steel Austenitic 600
and cast steel 260
160
Ferritic/ 250 15 80-140 0.02-0.08 0.015-0.05
130
Cast iron nodular (GG) pearlitic 230
Pearlitic/ 60
100 16 80-120 0.02-0.07 0.015-0.04
K Martensitic 75 17 80-140 0.02-0.08 0.015-0.04 0.02-0.10 0.05-0.12 0.04-0.10
Grey cast iron (GGG) Ferritic 90 18 80-120 0.02-0.07 0.015-0.04
Pearlitic 130 19 80-140 0.02-0.06 0.015-0.04
110 20 80-120 0.02-0.07 0.015-0.04
Malleable cast iron Ferritic 90 21 150-320 0.02-0.08 0.015-005
Pearlitic 100 22 100-250 0.02-0.08 0.015-005
23 150-300 0.02-0.08 0.015-005
Aluminum-wrought alloys Not cureable 200 24 150-300 0.02-0.08 0.015-005
Cured 280
250 25 100-150 0.02-0.08 0.015-005
<=12% Si Not cureable 350
320 26 80-230 0.02-0.08 0.015-005 0.02-0.10 0.05-0.15 0.05-0.12
Aluminum- Cured 27 70-200 0.02-0.08 0.015-005
55 HRC
cast-alloys >12% Si High 60 HRC 28 50-180 0.02-0.08 0.015-005
temperature
400
N >1% Pb Free cutting 55 HRC

Copper Brass

alloys Electrolitic

copper

Duroplastics, 29

Non-metallic fiber plastics

Hard rubber 30

Fe based Annealed 31 20-40 0.02-0.06 0.015-0.04

High temp. Cured 32 15-30 0.02-0.06 0.015-0.04
alloys Annealed
Ni or Co 33 15-20 0.02-0.06 0.015-0.04
S based Cured
Cast 34 15-20 0.02-0.06 0.015-0.04 0.015-0.7 0.02-0.08 0.02-0.05
35 15-20 0.02-0.06 0.015-0.04

RM 400 36 40-120 0.02-0.06 0.015-0.04

Titanium Ti alloys Alpha+beta RM 1050 37 20-50 0.02-0.06 0.015-0.04
alloys cured

Hardened steel Hardened 38
H Chilled cast iron Hardened 39
40
Cast 41

Cast iron Hardened