Page 78 - HOLE MAKING CATALOG p001-148
P. 78
USER GUIDE
Feed vs. Drill Diameter F [mm/rev]
INDEXABLE DRILLS
ISO
Hardness HB
Material No.(1)
26< ØD <28
29< ØD <32
33< ØD <35
36< ØD <43
44< ØD <50
Recommended Machining Conditions for MNC drills
Material Tensile Cutting
Strength Speed Vc
Condition [N/mm2] [m/min]
Vc Vc f f f f f f f f f f
min max min max min max min max min max min max
< 0.25 %C Annealed 420 125 1 120 200
≥ 0.25 %C Annealed 650 190 2
Non-alloy steel < 0.55 %C Quenched 850 250 3 0.25 0.35 0.25 0.35 0.25 0.40 0.25 0.40 0.28 0.45
and cast steel, and tempered
free cutting steel Annealed 750 220 4 130 190
≥ 0.55 %C Quenched 1000 300 5
and tempered
Annealed 600 200 6
P Low alloy and cast steel (less Quenched 930 275 7 120 180 0.25 0.33 0.25 0.33 0.25 0.38 0.25 0.38 0.26 0.43
than 5% of alloying elements) and tempered 1000 300 8
1200 350
9
High alloyed steel, cast Annealed 680 200 10
steel and tool steel 1100 325 11 100 160 0.25 0.33 0.25 0.33 0.25 0.36 0.25 0.36 0.26 0.41
Quenched
and tempered
Ferritic/ 680 200 12 90 140 0.12 0.24 0.12 0.24 0.16 0.25 0.18 0.25 0.18 0.30
Stainless steel and cast steel martensitic
Martensitic 820 240 13
M Stainless steel and cast steel Austenitic, 600 180 14 90 140 0.12 0.24 0.12 0.24 0.16 0.25 0.18 0.25 0.18 0.30
duplex
Gray cast iron (GG) Ferritic / 180 15
K pearlitic
260 16
Nodular cast iron (GGG) Pearlitic / 160 17 150 250 0.25 0.40 0.25 0.45 0.3 0.50 0.3 0.50 0.35 0.55
martensitic 250 18
Ferritic
Pearlitic
Malleable cast iron Ferritic 130 19
Pearlitic 230 20
Aluminum-wrought alloys Not 60 21
hardenable
Hardenable 100 22 160 260 0.3 0.50 0.3 0.50 0.35 0.55 0.35 0.55 0.4 0.60
Aluminum- ≤12% Si Not 75 23
cast alloys >12% Si hardenable 90 24
130 25
N Hardenable
High
temperature
>1% Pb Free cutting 110 26
Copper alloys Brass 90 27
100 28
Electrolytic
copper
Non metallic Duroplastics, 29
fiber plastics
Hard rubber 30
Fe based Annealed 200 31
Hardened 280 32
High temperature Annealed 250 33
Hardened 350 34
alloys Ni or Co 320 35
Cast
S based
Pure 400 36
Titanium alloys Alpha+beta 1050 37
alloys,
hardened
Hardened steel Hardened 55 HRC 38 20 50 0.1 0.16 0.12 0.18 0.14 0.2 0.14 0.2 0.16 0.22
H Chilled cast iron Hardened 60 HRC 39
40
Cast 400
Cast iron Hardened 55 HRC 41
(1) For workpiece materials list, see pages 495-524 . As a starting value, the middle of the recommended machining range should be used.
Then, according to the wear results, conditions can be changed to optimize performance.